FIELD: radio electronics. SUBSTANCE: method includes decomposing, in low-temperature air plasma stream, nitric acid zirconium solution and modifying additives, isolating product from dust-vapor-gas mixture at 470-560 C, cooling it to ambient temperature, mixing it with lead and titanium oxides, compressing prepared mixture into briquets at 950-1060 C for 40-120 min, and grinding resultant product. EFFECT: improved reproducibility of specified characteristics. 3 cl, 3 tblr
|