<p>Thermoplastic polymer blend compositions that include a thermoplastic matrix resin phase that is substantially free of cross-linking and a dispersed, silane-grafted elastomer phase are prepared by a multi-step process that begins with melt mixing a thermoplastic resin and an elastomer that have similar viscosities at temperatures used for melt mixing. A catalyst that promotes silane cross-linking, branching or both is preferably, but not necessarily, added to the melt mixed phases either while they are in a melt state or after they been recovered in a solid state. The melt mixed phases and the optional catalyst are then subjected to moisture, either before or after the melt mixed phases are converted to a shaped article, to effect branching and cross-linking within domains of the dispersed elastomer phase. The cross-linking and branching build elastomer molecular weight and stabilize dispersed domain shapes. The elastomer phase may contain a non-elastomeric polymer. A second, non-grafted elastomer phase may also be included in the thermoplastic polymer blend compositions.</p> |