摘要 |
A process for the production of a heat- and corrosion-resistant porous metal body which is made of a metal or whose surface layer is made of a metal, in which the porous metal body can be alloyed with chromium or a combination of chromium and aluminum uniformly throughout the entire thereof by adjusting the alloy composition in the following manner, i.e., (A) heat-treating the porous metal body in a mixed gas comprising a gas, generated by heating a powdered mixture comprising chromium or its compound and NH4Cl at 950 DEG to 1100 DEG C., and a diluent reducing gas at 800 DEG to 1100 DEG C, or (B) heat-treating the porous metal body in a mixed gas comprising a gas, generated by heating a powdered mixture comprising aluminum or its compound, chromium or its compound and NH4X, wherein X is I, F, Cl or Br, at a weight ratio of the chromium or its compound to the aluminum or its compound of 10 to 80 in terms of Cr and Al respectively at 950 DEG to 1100 DEG C., and a diluent reducing gas at 800 DEG to 1100 DEG C.
|