A borosilicate glass composition comprising 55-67 mol % of SiO2, 3-11 mol % of Al2O3, 16-26 mol % of B2O3, and 3-11 mol % of at least one oxide of SrO, CaO, MgO and ZnO is useful in the preparation of ceramic substrates. Since the amount of orthoboric acid formed on the glass in contact with humid air is minimized, the glass gives rise to little trouble in the manufacture of ceramic substrates. Ceramic compositions using the glass and a filler can be fired at low temperatures into sintered substrates which are characterized by a low dielectric constant, low dielectric dissipation factor, and high flexural strength.
|