| 摘要 |
Glass fiber reinforced thermoplastic resin composition is provided in this invention. Said thermoplastic resin composition is composed of (A), (B), (C) and (D) where (A) is 40 to 95 parts by weight of aromatic polycarbonate mainly composed of bisphenol A having melt index of 1 to 248/10min(ASTM D 1238), (B) is 5 to 60 parts by weight of glass fiber having at least 0.2mm of average length, (C) is 0.1 to 5 parts by weight of stareamide wax containing at least one of hydrogen, alkene or aromatic alkyl group and (D) is 0.01 to 5 parts by weight of phosphite containing at least one of alkyl group having 1 to 10 carbon atoms or aromatic alkyl group having 1 to 9 carbon atoms. Also, synthetic method of said resin composition is provided in this invention. (A), (C) and (D) prepared above are mixed at the entrance(2) of melt blender(1), then chopped (B) is blended with them at the discharger(3) to produce said glass fiber reinforced thermoplastic resin composition.
|