The invention concerns a method of manufacturing a black zirconia-based article, characterized in that it includes successive steps consisting of: producing a first mixture comprising a zirconia powder, 3 to 70% by weight of a stabilizer selected from the group of oxides comprising yttrium oxide, magnesium oxide, cerium oxide and calcium oxide, 1% to 10% by weight of a pigment selected from the group formed on the one hand by a cobalt oxide and iron oxide powder and on the other hand, by a spinel CoFe2O4 powder; producing a second mixture comprising said first mixture and a binder; producing a granulated mixture by granulating said second mixture; forming a rough model by giving said second granulated mixture the shape of the desired article; sintering in air for at least 30 minutes at a temperature less than 1,400 DEG C. when said pigment is a cobalt oxide and iron oxide powder and less than 1,600 DEG C. when the pigment is a spinel CoFe2O4 powder; and polishing said sintering said rough model.
|