SUPERPLASTIC ALUMINUM ALLOY AND PROCESS OF PRODUCING SAME

摘要

The present invention provides a superplastic aluminum alloy in which fine particles not substantially dispersion hardening are dispersed in a sufficient amount to effect grain boundary pinning to suppress crystal grain growth during hot working thereby ensuring manifestation of superplasticity over wide ranges of working temperature and strain rate. According to the present invention, a superplastic aluminum alloy contains ceramic particles having an average particle size of from 10 nm to 500 nm in an amount of from 0.1 vol% to 5 vol% and a process of producing a superplastic aluminum alloy, comprises the steps of: hot working an aluminum alloy ingot containing ceramic particles having an average particle size of from 10 nm to 500 nm in an amount of from 0.1 vol% to 5 vol% with a working degree of from 10% to 40% at a temperature of 400.degree.C or higher; heat-treating at a temperature of 400.degree.C or higher; and hot-working with a working degree of 40% or more at a temperature of lower than 400.degree.C.