| 摘要 |
The process puts a V6O13, a CuO, a trichloroethane(1,1,1-TCE), and a dispersing agent into a plastic tube, and then compounds four and sixteen alumina balls having a diameter of 3cm, 1cm respectively for two and half hours. After that, polyethylene oxide(PEO) and EPDM is added to it and compounded again for ten minutes. The solution dissolved through annexing a LiClO4, a ethylene carbonate(EC), and a propylene carbonate(PC) to a acetonitrile(ACN) is added to the compounded mixture, then they were compounded again for thirty minutes. After the mixture is coated on the Ni foil with the anode collection plate by making use of a doctor blade, then it is manufactured as a film by being dried at the normal temperature.
|