Non-oriented silicon steel sheet and method

摘要

A non-oriented silicon steel sheet having a low core loss contains Si in an amount of about 2.5-5.0 wt % and S restricted to about 0.003 wt % or less and inclusions; the volume ratio of those inclusions having a particle size of about 4 mu m or higher to the total volume of inclusions is about 5-60%, and the volume ratio of inclusions having a particle size less than about 1 mu m to the total volume of inclusions is about 1-15%; when the sheet contains Mn in an amount of about 0.4-1.5%, and the volume ratio of particles less than 1 mu m is about 1-5%, the silicon steel sheet also has a low rotation core loss. The method of manufacturing comprises controlling the change of a cooling speed to about 5 DEG C./s2 or less in the cooling process of such steel sheet in a finish annealing.