| 摘要 |
Mixes for forming high alumina refractory shapes with high resistance to aluminum penetration comprising at least about 60% by weight aluminum oxide, about 1 to 5% by weight boron phosphate, and about 5 to 15 % by weight silicon carbide. A phosphorous-containing binder is added and the mix can be formed into brick which when cured or burned to a temperature below the oxidation temperature of silicon carbide can be used to minimize aluminum penetration and dross when the brick are employed in a metallurgical vessel in contact with molten aluminum. |