VERFAHREN UND VORRICHTUNG ZUM GIESSEN VON METALL-MATRIX-VERBUNDMATERIAL

摘要

A composite material mixture of free flowing reinforcement particles in a molten metal is solidified at a cooling rate greater than about 15 degrees C. per second between the liquidus and solidus temperatures of the matrix alloy. This high cooling rate imparts a homogeneous structure to the solid composite material. Care is taken to avoid the introduction of gas bubbles into the molten composite material while the mixture is stirred to prevent segregation of the particles. For viscous melts, an artificial surface layer such as a fiberglass blanket may be used to prevent entrapment of bubbles during pre-casting stirring. Additionally, gas bubbles are removed from the molten mixture by filtering and skimming.