发明名称 |
INJECTION MOLDED ARTICLE MADE FROM PROCESSABLE THERMOPLASTIC POLYMETHACRYLATE |
摘要 |
PROBLEM TO BE SOLVED: To provide an injection molded product produced from a molding material based on polymethyl methacrylate and having excellent heat stability, good processability and high heat deformation resistance capable of becoming a comparing object. SOLUTION: A thermoplastically processable polymethacrylate molding material consisting of at least 80wt.% of a methyl methacrylate monomer unit and up to 20wt.% of a monomer copolymerizable therewith and having soln. viscosityηsp/c of 30-200ml/g is characterized by that heat deformation resistance (a) measured as Vicat softening temp. by DIN 53 460 is more than 120 deg.C, tacticity syndiotactic triad (b) is more than 60%, a TD value (2% depolymerization at heating rate 5 deg./min) (c) is more than 290 deg.C, light transmissivity (d) by DIN 1349 is more than 91% and residual monomer content (e) is less than 0.5% and produced by emulsion polymerization and the separation of water continued thereto (f). An injection molded part is produced from this polymethacrylate molding material. |
申请公布号 |
JPH09169042(A) |
申请公布日期 |
1997.06.30 |
申请号 |
JP19960316685 |
申请日期 |
1996.11.27 |
申请人 |
ROEHM GMBH |
发明人 |
BUERUNAA JIOORU;ERUNSUTO HAIRU;FURANTSU BUENTSUERU;PEETAA YOOZEFU ARUNTO;URURIHI TERUBURATSUKU |
分类号 |
C08J5/18;B29B11/00;B29C45/00;B29C47/00;B29K33/04;C08F2/22;C08F2/38;C08F6/06;C08F6/14;C08F6/22;C08F20/10;C08F20/14;C08J5/00;(IPC1-7):B29C45/00 |
主分类号 |
C08J5/18 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|