| 摘要 |
A dielectric ceramic composition comprising main components represented by a composition formula on the weight basis, aMgOxbCaOxcTiO2, wherein a, b and c satisfy the following relationships, 25</=a</=35, 0.3</=b</=7, 60</=c</=70, a+b+c=100, blended with a boron-containing compound in an amount of from 3 to 20 parts by weight reckoned as B2O3 and an alkali metal-containing compound in an amount of from 1 to 12 parts by weight reckoned as the alkali metal carbonate per 100 parts by weight of the main components, as well as a multilayer resonator made of said composition, and a filter using said resonator. The ceramic composition can be fired together with a conductor metal such as Ag or Cu at a relatively low temperature of 900 DEG to 1050 DEG C., exhibits large dielectric constant and Q-value, and a relatively small temperature coefficient tau f, lending itself well for use as a material for high-frequency electronic parts. The resonator made of this ceramic composition exhibits excellent tproperties in high-frequency regions, and can be realized in a small size.
|