| 摘要 |
The invention provides a sintered body for high-hardness tools which, when used for cutting work of cast irons where the cutting edge undergoes high temperature and abrupt impact, holds high chip-off and abrasion resistances and exhibits good cutting performance. The sintered body for high-hardness tools is obtained by sintering 60 to 75% by volume of cubic boron nitride powder and remaining part of a binder powder under a superhigh pressure, the binder comprising 5 to 15% by weight of Al, and the remaining part comprising a compound represented by (HfXTiyM1-x-y)(CZN1-z) alpha (where M denotes an element belonging to IVa, Va or VIa group in the periodic table except Ti and Hf, and where 0.1</=x</=0.5, 0.5</=y</=0.9, 0.7</=z</=0.9, and 0.6</= alpha </=0.8) or a mixture of a plurality of compounds that totally results in the aforementioned composition.
|