摘要 |
<p>The present invention provides a method for coating a titanium based component with diamond-like carbon to reduce the thrombogeneticity of the component. In a preferred embodiment, the titanium based component is a heart valve. According to the present invention, the component is placed in a vacuum chamber and heated to about 600°-650 °C (1112-1202 °F). Thereafter, silicon is then deposited onto the component, and the component is simultaneously bombarded with a beam of energetic ions to form a metal-silicide bonding layer. The component then is cooled to at least about 100 °C (212 °F), preferably about 80 °C (176 °F), and a diamond-like carbon precursor is condensed onto the metal-silicide bonding layer. The precursor is simultaneously bombarded with a beam of energetic ions to form a coating of diamond-like carbon.</p> |