| 摘要 |
PURPOSE: To provide the thermal spraying technique to a mold for continuous casting, particularly to the long sides thereof, in which even if fusing treatment after the thermal spraying is not executed, the high adhesion is obtained without exfoliating the film. CONSTITUTION: After forming Ni-electroplating having 0.1-2mm thickness to a part or the whole of the mold surface composed of copper or copper alloy, blast treatment is executed onto this plated surface so as to become 2-8 Ra roughness. Successively, after heating the mold at 50-100 deg.C, the thermal spraying of an Ni base self-fluxing alloy composed of (1) 60-80% Ni, 15-25% Cr, 1.5-5% B, 2-6% Si, 0.5-1% C, 3-4% Fe or (2) 5-10% Cr, 1.5-3.0% B, 2-4% Si, 0.09-0.60% C, 1.5-3.5% Fe and the balance Ni, and having 10-60μm grain diameter, is executed by using oxygen/hydrogen flame at 1300-2300m/s flame speed and thereafter, the film surface is finished to 1.6-6.3S Rmax. |