Disclosed are (i) a method of producing a support for planographic printing plate, which comprises melting an aluminum ingot having an aluminum content of not less than 99.7 wt % to prepare a cast ingot, scalping the surface of the cast ingot, soaking the scalped cast ingot, cold rolling the soaked ingot to a thickness of 0.1 to 0.5 mm, correction of the resulting sheet to prepare an aluminum support, and then graining the aluminum support and (ii) a method of producing a support for planographic printing plate, which comprises melting an aluminum ingot having an aluminum content of not less than 99.7 wt % to prepare a cast ingot in a melt holding furnace, directly subjecting the cast ingot to continuous casting to prepare a thin sheet having a thickness of 2 to 30 mm, cold rolling the thin sheet, correction of the resulting sheet to prepare an aluminum support, and then graining the aluminum support.
|