摘要 |
A method including preparing an aluminum scrap containing a total of about 0.3 to 2.0 wt % of Fe and Si; melting and then adjusting the material composition so as to attain an Mg content of about 3 to 10 wt % or a composition further containing at least one of the elements Cu, Mn, Cr, Zr and Ti, each in the amount of 0.02 to 0.5 wt %; subjecting the material to casting, hot rolling, cold rolling and continuous annealing to obtain an aluminum alloy sheet having a tensile strength of about 31 kgf/mm2 or more; and applying a lubricant surface coating to impart a coefficient of friction of not more than about 0.11.
|