ROOM TEMPERATURE VULCANIZABLE SILICONE COMPOSITIONS EMPLOYING PHENYL SUBSTITUTED TRIS-FUNCTIONAL KETOXIME SILANES

摘要

A room temperature vulcanizable silicone rubber composition with high elongation and low modulus comprising 10-90 percent by weight polydiorganosiloxane having terminal hydroxyl groups, 1-10 percent by weight phenyl tris-functional ketoximino-containing silane crosslinker, 0-14 percent by weight of a reinforcing or 0-60 percent by weight of a nonreinforcing filler or semi-reinforcing filler or a mixture thereof for a total of all fillers in the range of from about 6-60 percent by weight, from 0-2.5 percent by weight of an organofunctional silane adhesion promoter and an optional plasticizer and catalyst. These compositions cure to elastic materials useful as caulking materials, adhesives, coatings and encapsulating materials for the construction and other industries.