Hard anodic coating for magnesium alloys

摘要

A two-step process for the coating of magnesium and its alloys is disclosed. The first step comprises immersing the magnesium workpiece in an aqueous solution comprising about 0.2 to 5 molar ammonium fluoride having a pH of about 5 to 8 and a temperature of about 40 DEG to 100 DEG C. The second step is an electrochemical treatment of the pretreated article in an aqueous electrolytic solution having a pH of at least about 12.5 and which solution comprises about 2 to 12 g/L of a aqueous soluble hydroxide, about 2 to 15 g/L of a fluoride-containing composition selected from the group consisting of fluorides and fluorosilicates, and about 5 to 30 g/L of a silicate. This process results in a superior coating which has increased abrasion and corrosion resistance.