Cordierite honeycomb ceramics and method producing the same.

摘要

Cordierite honeycomb ceramics comprises a cordierite phase as a main ingredient. A value of [Fe2O3 wt%/(MgO wt%+Fe2O3 wt%)]x100 is 2-10, where a ferric component is calculated as Fe2O3. A thermal expansion coefficient of the cordierite honeycomb ceramics is less than 0.5x10<-><6>/ DEG C within a temperature range of 40-800 DEG C in a direction parallel to a flow passage of a honeycomb body. In the cordierite honeycomb ceramics including a ferric component, a ferric component is added from a talc as raw materials. The cordierite honeycomb ceramics having a low thermal expansion coefficient is obtained by mixing raw materials for cordierite generation to obtain a batch, extruding the batch into a honeycomb formed body, drying the honeycomb formed body, and firing the dried honeycomb formed body at a temperature range of 1350-1450 DEG C. After that, the sintered honeycomb body is immersed in an acid solution if necessary.