Disclosed is a spring steel for a high corrosion resistance and high strength, which exhibits an excellent drawability without softening heat treatment after hot rolling, and which has a strength of 1900 MPa or more by quenching and tempering and an excellent corrosion resistance. The spring steel contains, in mass %, 0.3-0.6% C, 1.0-3.0% Si, 0.1-0.5% Mn and 0.5-1.5% Cr, and 1.0% or less (excluding 0%) Ni and/or 0.1-0.5% Mo, the balance being essentially Fe and inevitable impurities, wherein the elements satisfy the following requirement: 2.5 </= (FP) </= 4.5 2.0 </= (FP/log D) </= 4.0 where D is a diameter (mm) of the rolled material, and FP = (0.23[C]+0.1)x(0.7[Si]+1)x(3.5[Mn]+1) x(2.2[Cr]+1)x(0.4[Ni]+1)x(3[Mo]+1) in which [element] represents mass % of the element. |
申请人 |
KABUSHIKI KAISHA KOBE SEIKO SHO |
发明人 |
KAWAGUCHI, YASUNOBU, C/O KOBE WORKS;SHIMOTSUSA, MASATAKA, C/O KOBE WORKS;MOMOZAKI, KAN, C/O KOBE WORKS;NAKAYAMA, TAKENORI, C/O KOBE CORPORATE RES. LAB.;MIYAUCHI, SHIGEAKI, C/O KOBE CORPORATE RES. LAB.;YAMAMOTO, YOSHINORI, C/O KOBE WORKS;OHKOUCHI, NORIO, C/O KOBE WORKS |