METHOD OF MANUFACTURING ARC WELDING BAR WIRE |
摘要 |
The method improves drawability of wire rods for CO2 gas arc welding electrodes without annealing treatment by controlling the amound of bainite and martensite. The method comprises; (A) hot rolling a billet with 0.07-0.1% C, 0.85-0.95% Si, 1.45-1.65% Mn, after homogenization treatment at 1050-1100 deg.C for 2 hours; (B) quenching to 820-840 deg.C by water injecting; (C) coiling and cooling to 760 deg.C with cooling rate of 2.3 deg.C per second; (D) slow cooling to 635 deg.C with cooling rate of 0.74 deg.C per second; and (E) air cooling to room temperature.
|