Gas barrier film and production process thereof.

摘要

Disclosed herein is a gas barrier film formed from a mixture containing polyvinyl alcohol and a partially neutralized product of poly(meth)acrylic acid in a weight ratio of 95:5 to 10:90, and having an oxygen permeability constant of 1.25 x 10<-><3> ml(STP).cm/m<2>. h.atm{Pa} or smaller as measured under conditions of 30 DEG C and 80% relative humidity. A production process of the gas barrier film, in which a film formed from a mixture containing polyvinyl alcohol and a partially neutralized product of poly(meth)acrylic acid is subjected to a heat treatment under specific conditions, is also disclosed. The gas barrier film of the invention is excellent in water resistance and oxygen gas barrier property, free of any chlorine atom, and scarcely colored. <IMAGE>