Water soluble polyvinyl alcohol-based fiber.

摘要

The process of the present invention comprises wet spinning or dry-jet-wet spinning a PVA-based polymer soluble in water at not more than 100 DEG C while using a dope solvent and a solidifying solvent each comprising an organic solvent, wet drawing the solidified filaments, subjecting the drawn filaments to extraction treatment and then drying, and further subjecting the filaments to heat shrinking treatment under multi-stage temperature elevation condition. The water soluble fibers of the present invention obtained by this process, while having a low water dissolution temperature of not more than 100 DEG C, have a markedly small maximum shrinkage in water and has high tensile strength and small ash content. The water soluble fibers of the present invention are suitably used for chemical lace base fabrics and blended yarns with wool or jute.