A glass fiber reinforced resin composition is prepared, the composition consisting essentially of: (1) 45 to 83% by weight of a crystalline ethylene-propylene block copolymer exhibiting a melt flow rate of 20 to 100 grams/10 minutes, comprising (i) an ethylene component in an amount of 3 to 12% by weight, and (ii) components having low molecular weights falling within the range of 1,000 to 50,000 in weight average molecular weight and soluble in chloroform at room temperature, in an amount of 0.3 to 3.5% by weight; (2) 2 to 20% by weight of a polypropylene resin modified with an unsaturated carboxylic acid derivative; and (3) 15 to 35% by weight of glass fiber. A wheel cap molded from the glass fiber reinforced resin composition has an excellent appearance, impact strength, rigidity, mechanical strength and thermal resistance, and can be manufactured at a low cost.
|