Method to enhance critical temperature of thallium-based superconductors

摘要

Unexpected results were obtained when Tl-1223 and Tl=-2223 superconductive materials were annealed at respectively pre-determined annealing temperatures. The optimum annealing temperatures for Tl-1223 and Tl-2223 superconductive materials are found to be 860 DEG C. and 820 DEG C., respectively. By incorporating the optimum annealing temperature and an optimum annealing envirenment, which is expressed in terms of oxygen partial pressure, into the manufacturing process, the present invention presents a method which can substantially increase the critical temperature of thallium based superconductive materials with greatly reduced annealing time and with improved reproducibility, and is thus superior to any method disclosed in the prior art.