发明名称 |
KNEADED REFRACTORY |
摘要 |
PURPOSE:To provide a monolithic refractory for cast molding previously kneaded with water added used for the wall lining of various molten metal vessels such as a tapping spout, a tundish for a blast furnace. CONSTITUTION:This monolithic refractory is produced by adding and kneading 0.1-3.0pts.wt. aluminum tripolyphosphate hardly soluble in water and 4-10pts.wt. water based on 100pts.wt. monolithic refractory prepared by mixing an alumina cement with an insulating material as a binder. As a result, the refractory causes hydraulic reaction at a relatively low temp. heating after working and is uniformly hardened. |
申请公布号 |
JPH06293569(A) |
申请公布日期 |
1994.10.21 |
申请号 |
JP19930078278 |
申请日期 |
1993.04.05 |
申请人 |
NIPPON STEEL CORP;NIPPON RUTSUBO KK |
发明人 |
SUZUKI TOSHIFUMI;KON MASARU;YOSHIDA TADAHIKO;INOUE NORIYUKI;SHIMIZU TAKASHI;OSAWA FUMIAKI |
分类号 |
B22D41/02;C04B28/06;C04B35/636;C04B35/66;F27D1/00 |
主分类号 |
B22D41/02 |
代理机构 |
|
代理人 |
|
主权项 |
|