| 摘要 |
Blister-resistant steel sheet consists essentially of 0.0005 to 0.003 wt. % C, 0.10 to 2.2 wt. % Mn, 0.6 wt. % or less Si, 0.07 wt. % or less P, 0.025 wt. % or less S, 0.02 to 0.06 wt. % of sol. Al, 0.0035 wt. % or less N, 0.003 wt. % or less O, [(48/14)N+(48/32)S+4x(48/12)C] wt. % or less Ti and the balance being Fe and inevitable impurities; and smaller one of either Ti (wt. %) or [(48/14)N+(48/32)S] (wt. %) being [0.002 t2+0.003] or more, where t is a thickness (mm) of the steel sheet. Method for producing blister-resistant steel sheet comprises preparing a cold rolled steel sheet having the composition of described above, and continuously annealing or continuous hot dip galvanizing by heating the steel sheet from room temperature to 650 DEG -720 DEG C. at a rate of 20 DEG C. sec or more and further to the soaking temperature above recrystallization temperature at a rate of 1 DEG -5 DEG C./sec.
|