PCT No. PCT/JP91/00779 Sec. 371 Date Feb. 6, 1992 Sec. 102(e) Date Feb. 6, 1992 PCT Filed Jun. 11, 1991 PCT Pub. No. WO91/19764 PCT Pub. Date Dec. 26, 1991.An olefin thermoplastic elastomer composition prepared by subjecting a composition comprising (a) 100 parts by weight of an ethylene- alpha -olefin-non-conjugated diene copolymer rubber having a high molecular weight, the Mooney viscosity (ML 1+4, at 125 DEG C.) of a composition consisting of 100 parts by weight of the copolymer rubber and 75 parts by weight of a mineral oil-type softening agent being 40 or more, (b) from 10 to 500 parts by weight of a crystalline ethylene-propylene block copolymer resin having a melt flow rate of 10 to 50, (c) from 3 to 300 parts by weight of a mineral oil-type softening agent, and (d) from 5 to 100 parts by weight of a low-molecular-weight propylene homopolymer resin having a number-average molecular weight of 2000 to 20000, the weight ratio of the low-molecular-weight propylene homopolymer resin to the crystalline ethylene-propylene block copolymer resin being 0.8 or less, to dynamic vulcanization using, as a vulcanizing agent, from 0.5 to 15 parts by weight of a reactive alkylphenol-formaldehyde resin to vulcanize the ethylene- alpha -olefin-non-conjugated diene copolymer rubber to a high degree.
|