METHOD OF PRODUCING BIMETAL FOR USE AS MATERIAL FOR PLAIN BEARING

摘要

There is disclosed a method of producing a bimetal for use as a material for a plain bearing. A copper alloy powder is placed on a back steel. The back metal and the copper alloy powder are preheated to a temperature near a Curie point of the steel in a reducing atmosphere by high-frequency induction heating. The preheated back steel and copper alloy powder are heated to a temperature of 770 DEG C. to 950 DEG C. in one of an electric resistance furnace and a gas furnace in a reducing atmosphere so that the copper alloy powder is sintered to form a sintered copper alloy layer and at the same time the sintered copper alloy layer is bonded to the back steel, thereby producing the bimetal.