摘要 |
A process for the production of a lanthanum chromite film, including the steps of preparing a plasma spray powder by mixing 1-15 parts by weight of powdery chromium oxide powder to 100 parts by weight of powdery lanthanum chromite, this lanthanum chromite having a composition ratio of A sites to B-sites being in a range of 1:1 to 1:0.9, forming a plasma sprayed film by plasma spraying the plasma spray powder onto a substrate, and forming the lanthanum chromite film by heat treating the resulting plasma sprayed film. The plasma spray powder may be produced by preparing a mixed powder by adding 1-15 parts by weight of powdery chromium oxide to 100 parts by weight of a synthesis powder capable of producing the lanthanum chromite film by heat treatment, the synthesis powder containing at least chromium oxide and lanthanum chromite and the lanthanum chromite film having a composition ratio of A-sites to B-sites being in a range of 1:1 to 1:0.9, obtaining a synthesized product by heating the mixed powder, and granulating the synthesized product.
|