Durch Elektroplattierung beschichteter Gegenstand, Verfahren zur Herstellung durch Elektroplattierung beschichteter Gegenstand sowie der dazu verwendete Elektrolyt.

摘要

An electro-deposition coated member comprises a substrate having thereon an electro-deposition coating film. The electro-deposition film contains a powder comprising a ceramic powder having an average particle diameter of from 0.1 to 5 mu m, the particle surfaces of which are coated with a metal, in an amount of from 5 to 50 parts by weight based on 100 parts by weight of the electro-deposition coating film. The electro-deposition coated member can be produced by a process comprising the steps of; subjecting a substrate to electro-deposition coating in a coating composition containing a resin feasible for electro-deposition and a powder comprising a ceramic powder having an average particle diameter of from 0.1 to 5 mu m, the particle surfaces of which are coated with a metal, the powder being contained in an amount of from 0.2 to 30 parts by weight based on from 100 to 150 parts by weight of the resin feasible for electro-deposition; and subsequently carrying out low-temperature curing.