A sputtered magnetic recording disk is formed by a series of sequential sputtering processes within an environment of a low pressure inert gas. A disk substrate is abraded to provide a circumferential texturing of hills and valleys. The height of the hills and valleys are of a dimension not to interfere with a fly characteristic of a recording head, while the arithmetic average of the radial roughness is still sufficient to provide a magnetic switching field distribution of less than 0.20. A chromium nucleating layer is deposited on the textured substrate surface by a first sputtering process. A second sputtering process provide a magnetic layer of a cobalt alloy to provide C-axis orientation parallel to the substrate. A third sputtering process provides a protective carbon film. The output of any signal recorded on the magnetic thin film layer will have an amplitude modulation of less than twenty-five percent (25%).
|