Aggregate treatment

摘要

The subject invention relates to a process for coating aggregate which is particularly useful in making asphalt concrete to provide the aggregate with a high level of resistance to stripping by water, which comprises: (1) mixing the aggregate with latex to form a latex/aggregate mixture which is comprised of from about 0.005 weight percent to about 0.5 weight percent dry polymer; (2) heating the latex/aggregate mixture to a temperature which is within the range of about 66 DEG C to about 232 DEG C; (3) maintaining the latex/aggregate mixture at said elevated temperature for a time which is sufficient to reduce the moisture content of the latex/aggregate mixture below about 0.7 weight percent and to allow the polymer in the latex to crosslink on the surface of the aggregate to produce the coated aggregate.