POROUS SHEETLIKE REFRACTORY AND ITS PRODUCTION |
摘要 |
PURPOSE:To obtain a sheet having low reactivity with a product without causing uneven burning by forming moderate pores and reducing the thickness in a porous sheetlike refractory used for burning electronic parts. CONSTITUTION:The objective porous sheetlike refractory is obtained by bonding 50-90 pts.wt. aggregate having >=30mum diameter composed of a refractory material with 10-50 pts.wt. inorganic binder having <=10mum diameter in a ceramic tool used for mainly burning electronic parts. Alumina, mullite, zirconia, magnesia, spinel or andalusite can be used alone or in combination with these aggregate and inorganic binder. The apparent porosity thereof is >=10% and its thickness is 0.3-5mm. The method for producing the sheetlike refractory is to form a green sheet by wet molding according to the extrusion or roll molding. |
申请公布号 |
JPH05310481(A) |
申请公布日期 |
1993.11.22 |
申请号 |
JP19920146528 |
申请日期 |
1992.05.12 |
申请人 |
MITSUI MINING & SMELTING CO LTD |
发明人 |
YAGISHITA TADASHI;ISSHIKI TOKUICHIRO;HORIUCHI KOJI;FUKUYAMA TOSHIYUKI;SUYAMA YUJI |
分类号 |
B28B3/12;B28B3/20;C04B35/00;C04B35/63;C04B35/64;C04B38/00;F27D5/00 |
主分类号 |
B28B3/12 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|