| 摘要 |
Provided are polyvinyl alcohol-based synthetic fiber having excellent performances as a fiber for FRC that is prepared by autoclave curing and its very effective production processes. One of the processes comprises having a monoaldehyde or a dialdehyde or its acetalization product penetrate into the central region of a polyvinyl alcohol-based synthetic fiber at a first stage and then, at a second stage, effecting crosslinking reaction with a mixed solution containing a monoaldehyde and an acid. The other process comprises conducting acetalization with a bath containing 100 to 250 g/l of formaldehyde and 30 to 80 g/l of sulfuric acid at a temperature of 70 to 100 DEG C. The processes can give a polyvinyl alcohol-based synthetic fiber having a strength of at least 11 g/d, a gel elasticity of at least 6.0 x 10<-><3> g/cm.d and a dissolution ratio of not more than 40% and being able to withstand an autoclave curing at 140 DEG C which is necessary for securing the dimensional stability of the resulting cement products. |