| 摘要 |
A partially crosslinked polymer composition having a melt flow index of from 0.1 to 50 g/10 min at 230 DEG C. under a weight of 2.16 kg and comprising a) a polymer comprising from 25 to 95% by weight of polypropylene and 5 to 75% by weight of a propylene copolymer with copolymerized C2-C10-alk-1-enes, the comonomer content being from 1 to 45% by weight, based on the total polymer, b) an organosilane compound of the formula (I) A4-nSiRn(i) where A are identical or different acrylates or methacrylates or vinyl groups, R are identical or different C1-C8-alkoxy or C1-C8-acetoxy groups, and n is 1, 2 or 3, obtainable by reacting the polymer a) with the organosilane compound b) in the presence of a free-radical initiator and in the presence of a condensation catalyst at from 180 DEG to 280 DEG C., and at from 1 to 100 bar and at a mean residence time of the reaction mixture of from 0.2 to 10 minutes, has, in particular, high notched impact strength, increased puncture resistance and improved weld line strength.
|