| 摘要 |
<p>Magnetic components having a higher permeability than those obtained from Ni-Zn-based ferrite powder can be obtained by molding a composition comprising 5 - 30 wt. parts of polyarylene sulfide resin and 70 - 95 wt- parts (providing 100 wt. parts with the resin) of Ni-Zn-Cu-based ferrite powder. The Ni-Zn-Cu-based ferrite has a composition represented by the following formula (1): NiaZnbCucFe2Od, wherein a, b, c and d are numbers satisfying 0.10 </= a </= 0.70, 0.10 </= b </= 0.80, 0.10 </= c </= 0.35 and 3.97 </= d </= 4.20.</p> |