| 摘要 |
An n-InP buffer layer 102, an InGaAsP active layer 103, a p-InP cladding layer 104 and a p-InGaAsP surface protective layer 105 are successively epitaxially grown on an n-InP substrate 101 having a (100) plane as a main plane. An etching mask 106, an insulating film, is formed in a stripe in the <011> direction by photolithography and dry etching. Using a solution comprising a mixture of hydrochloric acid, oxygenated water and acetic acid, the n-InP buffer layer 102 is etched to a depth lower than the p-InP cladding layer 103, to form a mesa stripe 107. Next, the insulating film 106 is removed and the p-InGaAsP surface protective layer 105 is removed using a solution comprising a mixture of sulfuric acid and oxygenated water. Thereafter, InP current blocking layers 108 and 109 are selectively formed at the regions other than the mesa stripe 107 by the liquid-phase epitaxial growth. Thus, a buried heterostructure semiconductor laser is fabricated, having good laser characteristics and a high reliability.
|