| 摘要 |
For the fabrication of casting rollers, casting roller shells and casting wheels, which, in casting close to the final dimensions, must be insensitive to a cyclically alternating temperature stress, materials of high thermal conductivity and high fatigue strength at the working temperature of the casting moulds are required. According to the invention, a hardenable copper alloy, which contains 1.0 to 2.6% of nickel, 0.1 to 0.45% of beryllium and, if appropriate, also 0.05 to 0.25% of zirconium, is proposed for this application. Preferably, the ratio of the nickel/beryllium contents is at least 5:1 and the nickel content above 1.2%. |