| 摘要 |
PURPOSE:To obtain a nonreducible dielectric porcelain compsn. in which sinters at a low temp. of <=1,080 deg.C and does not cause the deterioration of the electrical characteristics even by firing in a reducing atmosphere. CONSTITUTION:This nonreducible dielectric porcelain compsn. contains principal components represented by a general formula A(Bi2O3.BTiO2)+ (100- A)[(Sr100-X-YPbXCaY)(Ti100--zMgZ)O3] (where O<=A<=10mol%, 0.8<=B<=8mol%, O<=X<=100mol%, 0<=Y<=70mol% and 0.1<=X<=2mold%) and 0.1-30wt.% secondary components represented by a general formula aLi2O+bRO+cB2O3+(100'-b-c) SiO2 (where R is at least one among Mg, Ca, Sr and Ba, 0<=a<20mol%, 10<=b<55mol% and 0<=c<40mol%) and further contains 0.01-0.5wt.% MnO2. |