| 摘要 |
Novel aluminum bridged clays having an interfoliate spacing of at least 1 nm, well adapted as catalysts/catalyst supports, are prepared by (a) controlledly introducing an aqueous solution of a hydroxide base into an aqueous reaction medium containing suspended clay particulates and a dissolved aluminum salt, at a rate and for such period of time that the ratio of the concentration [C] of the base, in moles of OH- and expressed in moles/liter, to the duration (h) of introducing such OH- values, expressed in hours, is at least 0.1, and (b) recovering the reaction product bridged clay thus produced (and optionally drying/lyophilizing and/or calcining same).
|