| 摘要 |
<p>The invention consists of a process and device for the manufacture of crystallographically pure Zeolite 4A, making it possible, at will, to obtain any mean particle size between 2 and 5 microns, based on the crystallisation of an amorphous silicoaluminate gel formed by continuous reaction of an alkaline SiO2 dissolution of SiO2/Na2O molar ratio between 2.0 and 3.5, and another of Al2O3 in a gelifier reactor, with recycling of liquors and washing waters, respectively, to the Al2O3 and SiO2 digestors, crystallisation taking place in stages over a period of 30 to 90 minutes, at a temperature of 90 to 100 DEG C and with gentle agitation. <IMAGE></p> |