| 摘要 |
<p>The present invention provides a method of producing a hardened aluminum alloy sheet having superior thermal stability, the method comprising the steps of: homogenizing an ingot of an aluminum alloy consisting essentially of, in weight percentage, 3.0 to 6.0% Mg and 0.4 to 0.8% Mn, with the balance being Al and incidental impurities; hot rolling the homogenized ingot to a sheet; cold rolling the hot-rolled sheet at a rolling reduction of at least 20%; intermediate heat treating the cold-rolled sheet at 200 to 250 DEG C for one hour or more; and final cold rolling the intermediate heat-treated sheet at a reduction of at least 50%. In this process, the aluminum ingot may further contain from 0.05 to 0.4% Cu with or without 0.05 to 0.5% Si, 0.1 to 0.5% Fe, 0.01 to 0.05% Ti and 0.0001 to 0.0010% B. Further, the above homogenizing and hot rolling steps may be replaced by the steps of homogenizing, hot rolling to a sheet thickness of 2 to 6 mm, cold rolling and annealing for recrystallization.</p> |