发明名称 |
Preparation of pollucite ceramics. |
摘要 |
<p>The present invention is directed to a method for synthesizing highly crystalline pollucite articles at temperatures not exceeding 1650 DEG C. The method comprises two general steps: (a) a glass frit is prepared having a composition varying from approximately the stoichiometry of Cs2O.2SiO2 to approximately the stoichiometry of Cs2O.4SiO2 with, optionally, up to 5% Al2O3; and (b) that glass frit is reacted at a temperature between about 1000 DEG -1650 DEG C with an Al2O3-containing material in sufficient amounts to yield a final product having a stoichiometry approximating that of pollucite.</p> |