发明名称 |
PREPARING METHOD OF CARBON/CERAMIC COMPOSITE |
摘要 |
A carbon-ceramics composite is produced by (1) adding pitch system (isotropic and/or anisotropic) 10-40 wt.% with more than 300 deg.C of melting temperature as a carbon source, into a blast furnace water granulating slag 60-90 wt.% as a ceramic source, (the size of the mixed powder of the above pitch and slag is less than 0.074 mm), (2) pressure molding under the range of 100-500 kg/cm2 G, (3) heating the above molding material at a rate of less than 10 deg.C/ min in inert gas atmosphere, and (4) sintering the above (3) for 1 hour in the temperature range of 1,050-1,150 deg.C.
|
申请公布号 |
KR920005409(B1) |
申请公布日期 |
1992.07.03 |
申请号 |
KR19890020181 |
申请日期 |
1989.12.29 |
申请人 |
POHANG IRON & STEEL CO., LTD.;KOREA INDUSTRIAL TECHNOLOGY INSTITUTE |
发明人 |
PARK, YANG - DOK;LEE, SONG - YONG |
分类号 |
C04B35/52;(IPC1-7):C04B35/52 |
主分类号 |
C04B35/52 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|