| 摘要 |
PURPOSE:To make the title cloth flexible and lower hardness, by a method wherein specific laminated cloth which is a resin coating and comprised of woven fabric made of a high-tenacity synthetic fiber multi-filament and a polyolefin resin coating laminated to the woven fabric is formed under a specific condition. CONSTITUTION:A laminated cloth 1 which is comprised of a polyolefin resin coating and possesses basis weight of 150g/m<2> is laminated to woven fabric 2 made of a high-tenacity synthetic fiber multi-filament such as polyamide multi-filament or a polyester multi-filament. The resin coating is stuck to the surface of the woven fabric 2 and unified by melting of polyolefin resin. The resin coating 3 is formed in a continuing state so that permeability of the laminated cloth becomes not exceeding 2cc/cm<2>/min. Then prior to contact lamination adhesion increasing treatment is performed to either the woven fabric 2 or sheetlike resin or both of them and pressing treatment is applied to them after lamination. |