A single crystal shroud, preferably used around the high pressure turbine section of a gas turbine engine, has a composition, in weight percent, of from about 5 to about 10 percent chromium, from about 5 to about 10 percent cobalt, from 0 to about 2 percent molybdenum, from about 3 to about 10 percent tungsten, from about 3 to about 8 percent tantalum, from 0 to about 2 percent titanium, from about 5 to about 7 percent aluminum, from 0 to about 6 percent rhenium, from 0 to about 0.50 percent hafnium, from 0 to about 0.07 percent carbon, from 0 to about 0.015 percent boron, and from 0 to about 0.075 percent yttrium, balance nickel. The environmentally- resistant shroud preferably is used in the as-cast condition without any oxidation and corrosion resistant flowpath coating. |