| 摘要 |
PURPOSE:To enhance denitration activity and NOx removal capacity by forming a catalyst by making zeolite carry specific binary oxide, specific ternary oxide, oxide of W or Sn and one or more kind of Ce, Pr and Nd. CONSTITUTION:Zeolite is added to a cerium nitrate-containing aqueous solution to be mixed and kneaded therewith and the resulting mixture is dried at about 80-140 deg.C. Next, a solution prepared by dissolving ammonium para-tungstate in a monoethanolamine-containing aqueous solution and a molding aid are added to cerium carrying zeolite and a powder of TiO2.SiO2 to be mixed and kneaded therewith and the resulting mixture is molded into a honeycomb shape by an extrusion molding machine. The molded one is dried at about 50-120 deg.C and subsequently baked at about 400-700 deg.C for about 1-10hr in an air stream to obtain a nitrogen oxide removing catalyst. This catalyst efficiently reduces NOx to nitrogen and water at high temp. of about 400 deg.C or higher and has excellent durability. |